Appearance: | Liquid |
---|---|
Usage: | Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals |
Color: | Transparent |
Transport Package: | 20kg/ Carton Lined with Plastic Bags or Sheets |
Specification: | 20kg/ carton lined with plastic bags or sheets |
Trademark: | IOTA |
Samples: |
---|
Suppliers with verified business licenses
This product is manufactured with high-quality raw materials and has three series. Its special formula are designed for cable accessories and the molded or extruded products requiring some strength in ordinary industries. The product is corona-resistant and arc-resistant, with stable weatherability and electrical insulating property. It has high transparency and physical & mechanical properties. The rubber for molding is vulcanized with 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane as vulcanizing agent and the rubber for extrusion is vulcanized with vulcanizing agent DCBP (Di-(2,4-dichlorobenzoyl) Peroxide), particularly applicable to manufacturing of various wall bushings, cable accessories, electrical insulation products and other industrial products.
T
Typical Properties:
Category |
Item |
Appearance |
Hardness Shore A |
Tensile strength MPa≥ |
Elongation at break %≥ |
Breaking set %≤ |
Tear strength B KN/m≥ |
Specific density 25°C g/cm³ |
Compression set 180*22h %≤ |
Resilience %≥ |
For molding |
IOTA |
Ivory Translucent |
40±2 |
7.5 |
450 |
5 |
20 |
1.12±0.05 |
20 |
5.0 x 10¹ |
IOTA D345 |
45±2 |
8.0 |
420 |
6 |
20 |
1.14±0.05 |
20 |
5.0 x 10¹ |
||
IOTA D351 |
50±2 |
8.0 |
400 |
6 |
20 |
1.16±0.05 |
20 |
5.0 x 10¹ |
||
IOTA D3140 |
40±2 |
7.5 |
450 |
5 |
20 |
1.12±0.05 |
20 |
5.0 x 10¹ |
||
IOTA D3150 |
50±2 |
8.0 |
400 |
6 |
20 |
1.16±0.05 |
20 |
5.0 x 10¹ |
||
IOTA D3160 |
60±2 |
8.0 |
300 |
9 |
20 |
1.20±0.05 |
20 |
5.0 x 10¹ |
Physical data in the above table is for reference only.
Vulcanization condition: 175ºC× 5Min.
Ratio of curing agent 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane:0.65%.
Advantage:
- Good processability
- Excellent comprehensive physical properties
Applications:
- Cable joints, sheaths and accessories
Category |
Item |
Appearance |
Hardness Shore A |
Tensile strength MPa≥ |
Elongation at break %≥ |
Breaking set %≤ |
Tear strength B KN/m≥ |
Specific density 25°C g/cm³ |
Compression set 180*22h %≤ |
Resilience %≥ |
For extrusion |
IOTA D3250 |
Ivory Translucent |
52±2 |
8.5 |
420 |
10 |
20 |
1.18±0.05 |
20 |
5.0 x 10¹ |
IOTA D3260 |
62±2 |
8.0 |
300 |
9 |
20 |
1.20±0.05 |
20 |
5.0 x 10¹ |
||
IOTA D3270 |
72±2 |
7.5 |
260 |
9 |
20 |
1.22±0.05 |
20 |
5.0 x 10¹ |
Physical data in the above table is for reference only.
Vulcanization condition: 175ºC× 5Min.
Ratio of curing agent 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane:0.65%.
Advantage:
- Good processability
- Excellent comprehensive physical properties
Applications:
- Various silicone rubber tubes, conduits, heat-resisting sealing strips, wires and cable sheaths.
Packing & Storage:
- 20kg/ carton lined with plastic bags or sheets.
-The products have a shelf life of 9 months from date of manufacture depending on the shore hardness if stored at room temperature in the originally sealed container.Suppliers with verified business licenses