IOTA FLSR8520 Fluorosilicone Coating Solution
Description:
IOTA FLSR8520 fluorosilicone coating solution is an adhesive-type liquid fluorosilicone material, has excellent adhesion, oil resistance, high and low temperature resistance, and hydrophobicity. It can be used for bonding and surface modification of various substrates, such as PET, PA, chemical fibers, fiberglass, leather, metals, etc. During use, organic solvents can be added for dilution, imparting excellent surface properties to the material after immersion or spraying.
Product performance:
|
Item |
Test Methods |
IOTA FLSR8520 |
|
Component A color |
Visual inspection |
translucent |
|
Component B color |
Visual inspection |
translucent |
|
The mixing ratio |
Q/371002WXH015-2017 |
1:1 |
|
Mixed viscosity/mPa.s (25ºC) |
Q/371002WXH015-2017 |
50~5000 |
|
Operating time/h(25ºC) |
Q/371002WXH015-2017 |
2~4 |
|
Solid content/% |
Q/371002WXH015-2017 |
30~70 |
|
density/g/cm3 |
ASTM* D792 |
1.02~1.40 |
|
hardness/Shore A |
ASTM D2240 |
22 |
|
Tensile Strength/MPa |
ASTM D412 |
3.0 |
|
Elongation at break/% |
ASTM D412 |
265 |
|
Tear strength/kN/m |
ASTM D624-B |
10.2 |
|
Shear strength(PET) |
GB/T 7124 |
100% cohesive destruction |
Usage:
IOTA FLSR8520 fluorosilicone coating solution is packaged in two components. When in use, components A and B can be mixed in a 1:1 weight ratio by mass and applied directly. Alternatively, according to process requirements, an appropriate amount of organic solvent can be added to the material for dilution before application.
Packaging:
Packed in 10kg plastic drums.
Shelf Life:
Store in a cool, dry environment in, shelf life is 6 monthes in unopened original packaging.
Precautions:
Avoid contact with compounds containing nitrogen, sulfur, phosphorus, and heavy metals to prevent incomplete vulcanization or non-vulcanization of the product.