Low Viscosity and Easy Automatic Feeding Special Coating Liquid Silicone Rubber Iota M1730 for Airbag, Protective Clothing

• Customization: Available
• Material: Organic Silicone
• Application: Household, Medical, Industrial
• Model NO.: Iota M1730
• Certification: ISO, FDA, REACH, RoHS
• Density: 1.07 g/cm3
• Hardness: 30
• Tensile Strength: 5.0 MPa
• Elongation at Break: 400%
• Transport Package: Drum
• Specification: 200kg
• Trademark: Iota
• Origin: Anhui Bengbu
• HS Code: 39100000
• Production Capacity: 1000tons
• Package Size: 13.00cm * 13.00cm * 15.00cm
• Package Gross Weight: 2.000kg

Product Description

Special coating liquid silicone rubber for airbag IOTA M1730

Description
IOTA M1730 A/B is a special coating liquid Silicone rubber for airbag with self-adhesive properties to PA66.  

Advantages
Excellent self adhesion to PA66 
low viscosity and easy automatic feeding 
Rapid heat curing
long operation time after mixing
Excellent mechanical properties

Application
Airbag coating
Architectural textile coating
Protective clothing coating
3C product sealing, etc

Curing condition
Temperature: 160°C
Curing time:T90 less than 25s

Note
IOTA M1730 A/B is a product catalyzed by platinum product. The platinum catalyst is in the component A. Strict attention should be paid when using, to avoid catalyst poisoning.

Packing and storage
Component A:200kg/iron drum, component B:200kg/iron drum

Storage

1. Below 23°C, unopened barrels can be stored for 12 months, and the best use-by date is marked on the label of each product's outer packaging.

2. After the expiry date, it is necessary to do performance tests for relevant indicators to ensure the quality, and then could be used.

Technical index

Properties	Test method	Value
Unmixed
Component A
Color		slight yellow
Density		1.07 g/cm^3
Viscosity at 25ºC,0.9S^-1	Brookfield	45000 mPa.s
Component B
Color		slight blue
Density		1.07 g/cm^3
Viscosity at 25ºC,0.9S^-1	Brookfield	53000 mPa.s
Technical data(A+B mixed)
Mix ratio(weight)	A:B	1:1
Viscosity at 25ºC,0.9S^-1	Brookfield	52000 mPa.s
Curing time		See curing conditions
Technical data(cured)	165±2ºC*300 S
Color		slight yellow
Density at 23ºC	DIN EN ISO 1183	1.07 g/cm^3
Hardness	DIN ISO 48-4	30
Tensile strength	ISO 37 type 1	5.0 Mpa
Elongation at break	ISO 37 type 1	400%
Tear strength	ASTM D 624 B	10 KN/m

Q1: What is Liquid Silicone Rubber (LSR)?
A1: LSR is a high-purity, two-part platinum-cured elastomer. It starts as a liquid and cures into a durable, flexible silicone rubber with excellent thermal stability and chemical resistance.

Q2: What are common applications for LSR?
A2: It's widely used for making medical devices (like seals and tubing), baby products (nipples), kitchenware, automotive parts, and flexible seals for electronics due to its safety and durability.

Q3: How is LSR processed?
A3: LSR is typically processed using liquid injection molding (LIM). Its two components (base and catalyst) are pumped, precisely mixed, and then injected into a heated mold where it cures quickly.

Q4: What are the key advantages of LSR?
A4: Its main advantages are excellent biocompatibility, high temperature resistance (from -50°C to over 200°C), good electrical insulation, and the ability to be molded into complex, precise parts.