Post Cured Free High Bite Force Liquid Silicone Rubber Iota M6040K for Baby Care/Food Contact/Sealing Ring/Other Injection Products

• Appearance: Liquid
• Usage: Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
• Color: Transparent
• Density 23ºC: 1.12 g/cm3
• Viscosity 23ºC, 10s-1: 320 PA.S
• Density 23&Ordm: 1.12 g/cm3
• Model NO.: Post cured free high bite force liquid silicone ru
• Viscosity 23ºC,0s-1: 280PA.S
• Transport Package: a Component 200 Kg/Drumb Component 200 Kg/Dum
• Specification: A component 200 Kg/drumB component 200 Kg/dum
• Trademark: iota
• Origin: Bengbu Anhui China
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

Post cured free high bite force liquid silicone rubber IOTA M6040K

 

Description

IOTA M6040K A/B is a high bite force liquid silicone rubber free of post cured.

 

Features

Two-component, 1:1 mixing ratio

Excellent mold release

VOC less than 0.5%

Fast thermal curing

Excellent mechanical properties

Comply with BfR, FDA, ROHS requirements

Application

Baby care

Food contact

Sealing ring

Other injection products, etc.

 

Curing:

The curing time of addition products is largely temperature dependent.

Temperature	Curing time, 2mm thickness
130ºC	90 S
150ºC	45 S

 

 

Notes:

IOTA M6040K A/B is a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.

Only same batch of components A and B could be mixed together.

In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.

 

Technical data

Properties	Test method	Value
Uncured products
Component A
Color		Transparent
Density 23ºC		1.12 g/cm^3
Viscosity 23ºC, 10S^-1	ISO3219	320 Pa.s
Component B
Color		Transparent
Density 23ºC		1.12 g/cm^3
Viscosity 23ºC, 10S^-1	ISO3219	280Pa.s
Product data (A+B mix)
Mixing ratio (weight)	A:B	1:1
Viscosity 23ºC, 10S^-1	ISO3219	300Pa.s
Curing time		See curing conditions
Product data (after curing)	(125±2ºC, cured for 5min)
Color		Transparent
Density 23ºC		1.11 g/cm^3
Hardness	DIN 53505	40
Tensile Strength	DIN 53504	9 MPa
Elongation	DIN 53504	580 %
Tear strength	ASTMD 624B	35 KN/m

 

Packaging & storage

A component 200 Kg/drum,B component 200 Kg/dum.

Store under 23ºC to avoid exposure to rain and sunlight.

Shelf life: 12 months, unopened condition.