Iota Flsr8400 Series Addition Formed Liquid Fluoro Silicone Rubber

• Molecular Principal Chain: Element Organic Polymer
• Color: Faint Yellow and Translucence
• a Component Viscosity / PA.S (Shear Rate: 700/820
• Model NO.: IOTA FLSR8400
• B Component Viscosity / PA.S (Shear Rate: 650/770
• Density/g/cm3: 1.42/1.43
• Tensile Strength/MPa: 11.0/7.9
• Transport Package: Plastic Drum
• Specification: 20kg
• Trademark: IOTA
• Origin: China
• HS Code: 3910000000
• Production Capacity: 100mt/Month

Product Description

IOTA FLSR8400 Series Addition formed liquid fluoro silicone rubber

Description: 
IOTA FLSR8400 series two-component additive liquid fluorosilicone rubber is made of polyfluorosiloxane containing vinyl as the base adhesive, oligofluorosiloxane containing hydrogen siloxane as the crosslinking agent, reinforced by filler, using platinum vulcanization system of liquid polymer material. With excellent high and low temperature resistance, oil resistance and electrical insulation, can maintain long-term stability in harsh environments, fast and convenient molding, short processing cycle, wide temperature, very suitable for the production of oil resistant parts in the fields of automotive, Marine, aerospace, power and electrical, in addition, it can be further expanded to consumer electronics, wearables and healthcare, etc. The application prospect is broad.

Product performance :

Item		Test method		IOTA FLSR8440		IOTA FLSR8460
A Component color		visual inspection		Faint yellow		Faint yellow
B Component color		visual inspection		Translucence		Translucence
A Component viscosity / Pa.s (shear rate 10 s^-1)		Q/371002WXH028-2016		700		820
B Component viscosity / Pa.s (shear rate 10 s^-1		Q/371002WXH028-2016		650		770
120ºC×10min After the first vulcanization
Density/g/cm^3	ASTM* D792		1.43		1.42
Hardness/Shore A	ASTM D2240		39		59
Tensile strength/MPa	ASTM D412		11.0		7.9
Elongation at break/%	ASTM D412		425		235
Tearing strength/kN/m	ASTM D624-B		15		13
Rebound resilience/%	ASTM D1054		40		41
Compression set/%(177ºC×22h)	ASTM D395		10		20
200ºC×4h After the second vulcanization
Hardness/Shore A	ASTM D2240		40		62
Tensile strength/MPa	ASTM D412		10.8		7.2
Elongation at break/%	ASTM D412		368		181
Tearing strength/kN/m	ASTM D624-B		14		13
Rebound resilience/%	ASTM D1054		41		43
Compression set/%(177ºC×22h)	ASTM D395		4		6
Oil resistance
Dextron III/%(125ºC×168h)	ASTM D471		1.1		1.2
IRM903/%(150ºC×168h)	ASTM D471		2.2		2.0
IRM903/%(150ºC×168h)	ASTM D471		2.2		2.0
RME Biodiese l/%(40ºC×168h)	ASTM D471		3.1		3.2
Fuel F Diese l/%(40ºC×168h)	ASTM D471		3.3		2.4
Fuel C/%(60ºC×168h)	ASTM D471		22.2		20.5
FAM B/%(60ºC×168h)	ASTM D471		28.8		28.0
Jet Fuel No.3/%(23ºC×168h)	ASTM D471		4.9		5.1

Usage:
IOTA FLSR8400 series liquid fluorosilicone rubber is A two-component material, divided into A/B two components, separately packaged.
When in use, the A and B components are mixed evenly in the three-roll grinder or planetary mixer according to the mass ratio of 1:1, and then defoamed, moulded, coated vulcanized, and vulcanized by injection molding machine can be directly manipulated according to the platform.

Conditions of vulcanization:
The vulcanization time of IOTA FLSR8400 series liquid fluorosilicone rubber depends on the vulcanization temperature and the thickness and size of the vulcanization product. When the vulcanization product is heated to 120ºC, it can be vulcanized rapidly in a few seconds. The rate can be optimized according to the component size. Please adjust the curing time reasonably according to the actual production process.

Package:
Plastic drum packing, A/B components 20kg each separately packed.

Storage period:
Store in a cool and dry environment, unopened original package storage period of 12 months.
 
Attention:
Avoid contact with compounds containing nitrogen, sulfur, phosphorus and heavy metals, so as not to cause immature or unvulcanized products.