High Bite Force Addition Type Liquid Silicone Rubber Iota M4240K for Nipple

• Material: Organic Silicone
• Application: Household, Medical, Industrial, Agricultural
• Hardness: 40-60
• Transport Package: 25 Kg, 200 Kg Drums, or 1000 Kg IBC Tank
• Trademark: Iota
• Origin: Anhui Bengbu
• HS Code: 39100000
• Production Capacity: 1000tons

Product Description

   High bite force addition type liquid silicone rubber series of IOTA M4240K
Description:
IOTA M4240K A/B series is a food grade,high bite force addition type liquid silicone rubber.

Features:
1. Two-component, 1:1 mix ratio
2. Excellent mold release
3. Fast heat curing
4. Excellent mechanical properties


Application:
1. Miscellaneous parts
2. Nipple
3. Various injection molding miscellaneous products
4.Complex structure injection products

Curing:

temperature	Curing time, 2mm thickness
130ºC	90 S
150ºC	45 S

Technical data:

Properties	M4240K	M4250K	M4260K
Uncured products
Component A
color	transparent
Density 23ºC,g/cm^3	1.12	1.12	1.12
Viscosity 23ºC, 10S-1	300Pa.s	300 Pa.s	320Pa.s
Component B
color	transparent
Density 23ºC,g/cm^3	1.12	1.12	1.12
Viscosity 23ºC, 10S-1	280Pa.s	290 Pa.s	300Pa.s
Technical data(A/B mixed)
Mixing ratio (weight)	1:1
Viscosity 23ºC, after stirring	300Pa.s	300 Pa.s	320Pa.s
curing time		see curing conditions
Technical data(cured)	(125±2ºC, 5min)
color	transparent
Density 23ºC,g/cm^3	1.12	1.12	1.12
Hardness	40	50	60
Tensile Strength	9Mpa	10 Mpa	10 Mpa
Elongation	550%	550 %	500 %
tear strength	30KN/m	40 KN/m	38 KN/m

NOTES
1. IOTA M4240K A/B series is a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
2. Only same batch of components A and B could be mixed together.
3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.

Packaging & storage   
A component 200 Kg/drum,B component 200 Kg/dum.
Store under 23ºC to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.