Audited Supplier Perhydropolysilazane (PHPS) or Inorganic Polysilazane IOTA-PHPS
Name: Hydrophilic Super Hard Stain Resistant Nano-Coating Materials
English synonyms: PHPS
Polysilazane Liquid Coating Materials
Description:
The coating product is mainly composed of perhydropolysilazane IOTA PHPS,diluted and stored in a solvent.
Features:
Good solubility
Short curing time
Curing a variety of ways
Good adhesion on the metal ceramic polymer materials
Can be converted to SiO2 at a lower temperature
Technical Parameters:
| Appearance: | colorless transparent liquid |
| Solid content: | 20% |
| Solvent: | butyl ether |
| Liquid density: | 1.16-1.31 g / ml |
| Density after curing: | 1.6-2.0 g / ml |
Curing mechanism:
The curing of the coating material mainly is the Si-N bond hydrolysis, the mechanism is as follows:
Curing conditions:
Room temperature: more than 7 days
Moisture curing: humidity 90%, temperature 150 ºC, 2h Rust, alkali, salt water resistance
Coating properties:
| Composition: | SiOx |
| Coating thickness (nm): | >100 |
| Hardness (GPa): | 3 (ammonia curable) 8-10 (high temperature curing) |
| Elastic modulus (GPa): | 60 (NH3.H2O curing) 100-130 (high temperature curing) |
| Pencil Hardness: | 9H(Chinese) 6H (Mitsubishi) |
| Transparency (visible light): | > 90% |
| Adhesion (grid method): | 0 level |
| Temperature resistance (air): | 800 ºC |
Applications:
Building anti - graffiti
Metal anti-corrosion
Rail
Semiconductor insulating layer
electronic circuit
Plastic packaging waterproof gas barrier
Metal high temperature oxidation resistance
Surface hardening coating
Product packaging:
According to customer demand, 0.5-10 liters metal sealed drum, generally use xylene, dibutyl ether or dichloromethane for filling, solid content of 2-20%.
How to use:
First, clean the substrate surface, coating products using spin-coating, rubbing, spraying, dipping, etc. construction, and then by room temperature curing, high temperature curing, etc. curing.
Clean:
Proper cleaning is important. After using promptly use acetone or solvent oil to wipe the tool cleaning.
IOTA PHPS cured, the solvent can not be washed away.
Storage:
Shelf life: 2years; after the application, it depend on the protective measures, sealed low temperature drying case, the applicable period of more than half a year.
Acid (10% hydrochloric acid): about a month.
Precautions:
Should l be in a ventilated, dry environment, and the use of necessary protective measures, such as gloves, masks, goggles; shall not
Do not place uncured IOTA PHPS near to fire, humid air, or water.