Liquid Silicone Rubber Iota LSR 32p-1series for Leather

• Material: Organic Silicone
• Application: Household, Industrial
• Certification: ISO
• Model NO.: IOTA LSR 32P-1
• Hardness: 10-60
• Viscosity: 3000-5000
• Tensile Strength: ≥7.0
• Transport Package: Drum
• Specification: 200kg
• Trademark: Iota
• Origin: Anhui
• HS Code: 39100000
• Production Capacity: 800 Tons/Month

Product Description

Liquid silicone rubber for leather
Coating liquid silicone rubber IOTA LSR 32P-1Series

Description
The IOTA LSR 32P-1 series is a specialized coated liquid silicone rubber used for the production of leather.

Advantage
Good release
High strength
Low viscosity, good fluidity, easy to operate

Application
Car/sofa seats
Luggage, shoes, and clothing
Baby cushion
Other leather products

Technical Data

Item	Unit	Type	Testing standards
		IOTA LSR 32P
Appearance	-	Transparent	Visual
Viscosity	mPa.s	3000-5000	ASTM D2209-00
Tensile strength	MPa	≥7.0	ASTM D2209-00
Elongation	%	≥400	ASTM D2209-00
Hardness	(ShoreA)	10-60	ASTM D2209-00
Tear strength	KN/m	10-40	ASTM D2209-00

This is base silicone rubber, customers can adjust the number of coatings according to actual requirement.
The surface layer can choose the hand feel oil (which can increase the leather surface feel) to produce end products.

Note:
1. Typical values: The parameters may vary depending on the specific silicone type and formula.
2. Testing standards: can be adjusted according to customer requirements or industry standards.
3. Customized parameters: such as color, hardness, temperature resistance range, etc., can be customized according to customer requirements.


4. The above data is for reference only.

Usage
1) Mixing ratio: 1:1 mix and Vacuum treatment.
2) Curing conditions: Coated liquid silicone rubber will quickly cure in high temperature environments. The curing time depends on the thickness and the curing temperature used. Contact with certain materials such as amine, sulfur, and tin compounds can inhibit curing.
3) Curing conditions: (120-140) ºC for (3-5) minutes.
4) Operation time: After mixing components A and B, the effective period of the mixture at 25 ° C is 48 hours.

Clean
Most hydrocarbon solvents can remove uncured silicon. However, polar solvents such as ketones and ethanol cannot be removed.

Packaging and storage
1) Packaging: 20kg/barrel, 200kg/iron drum
2) The product should be stored in an unopened original container at a temperature of 32 ° C or lower.
3) This product has a storage period of 12 months and can still be used after passing the re inspection beyond the expiration date.