| Material: | Organic Silicone |
|---|---|
| Application: | Household, Medical, Industrial, Agricultural |
| Certification: | ISO, FDA, REACH, RoHS |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Description
IOTA M6070 A/B is a liquid silicone rubber free of post cured.
Features
Two components, 1:1 mixture ratio
Excellent mold release
VOC is less than 0.5%
Rapid heat curing
Excellent mechanical properties
Meet the requirements of BfR,FDA and ROHS
Aapplication
Baby care
Food contact
Sealing ring
Other injection products, etc.
Curing
|
Temperature |
Curing time,2mm thickness |
|
130ºC |
90 S |
|
150ºC |
45 S |
NOTES
IOTA M6070 a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.
Only same batch of components A and B could be mixed together.
In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.
Technical data
|
Properties |
Test method |
Value |
|
Uncured products |
|
|
|
Component A |
|
|
|
color |
|
transparent |
|
Density (23ºC) |
|
1.14 g/cm3 |
|
Viscosity (23ºC,10S-1) |
ISO3219 |
380 Pa.s |
|
Component B |
|
|
|
color |
|
transparent |
|
Density (23ºC) |
|
1.14 g/cm3 |
|
Viscosity (23ºC,10S-1 ) |
ISO3219 |
350 Pa.s |
|
Technical data(A/B mixed) |
|
|
|
Mixture rate(weight) |
A:B |
1:1 |
|
Viscosity(23ºC,10S-1) |
ISO3219 |
380 Pa.s |
|
Curing time |
|
See curing conditions |
|
Technical data(cured) |
(125±2ºC, 5min) |
|
|
color |
|
transparent |
|
Density (23ºC) |
ISO2781 |
1.14 g/cm3 |
|
Hardness |
DIN 53505 |
70 |
|
Tensile strength |
DIN 53504 |
9 Mpa |
|
Elongation |
DIN 53504 |
340% |
|
Tear strength |
ASTMD 624B |
32 KN/m |
Packaging & storage
A component 200 Kg/drum,B component 200 Kg/dum.
Store under 23ºC to avoid exposure to rain and sunlight.
Shelf life: 12 months, unopened condition.