Self Adhesive Liquid Silicone Rubber Iota M3060 for Goggle Seal Parts

• Material: Organic Silicone
• Application: Household, Medical, Industrial, Agricultural
• Hardness: 60
• Transport Package: 25 Kg, 200 Kg Drums, or 1000 Kg IBC Tank
• Trademark: Iota
• Origin: Anhui Bengbu
• HS Code: 39100000
• Production Capacity: 1000tons

Product Description

Self adhesive liquid silicone rubber IOTA M3060 AB
Description
IOTA M3060 A / B is a kind of liquid silicone rubber with self-adhesive to PC and good mold release properties.
Features
1. Two component,1:1 mixing ratio.
2. Excellent mold release performance.
3. Excellent self adhesion to PC.
4. Rapid thermal curing.
5. Excellent mechanical properties.

Applications
1. Goggle seal parts
2. Mobile phone case rubber coating
3. Smart watch rear cover sealing parts
4. Mobile phone SIM card sealing parts

Notes

1. IOTA M3050J is a platinum catalyzed product. The platinum catalyst is in the component A. Strict attention should be paid when using, to avoid catalyst poisoning.
2. If you want to add color, be sure to add color to component B, stir it evenly, and then mix with quantitative agent A.
3. To ensure optimum fluidity and homogeneity of the material, the material must be thoroughly agitated before being transferred to the container.

Technical index:

Properties	Test Method	Value
uncured
Component A
Color		transparent
Density 23°C,10S^-1		1.138 g/cm^3
Viscosity at 23ºC, stirred	ISO3219	300 Pa.s
Component B
Color		Translucent
Density 23°C,10S^-1		1.138 g/cm^3
Viscosity at 23ºC, stirred	ISO3219	500 Pa.s
Product data (A+B mixed)
Mixing ratio (weight)	A:B	1:1
Viscosity at 23ºC, stirred	ISO3219	400 Pa.s
Curing time		See the curing condition
Product data (after cured)	(125±2°C,After 200s curing time)
Color		Transparent
Density 23°C	ISO2781	1.138 g/cm^3
Hardness (Shore A)	DIN 53505	60
Tensile Strength	DIN 53504	10 MPa
Elongation	DIN 53504	450 %
Tear strength	ASTMD 624B	40 KN/m
PC Cohesive failure≥50%	/	Qualified

Packaging
Component A: 20 Kg/drum, component B: 20 Kg/drum.

Curing condition

Temperature	Curing time,1cm thickness
125°C	200 S
150°C	50 S

Storage   

1. Below 23°C, unopened barrels can be stored for 12 months, and the best use-by date is marked on the label of each product's outer packaging.

2. After the expiry date, it is necessary to do performance tests for relevant indicators to ensure the quality, and then could be used.