| Customization: | Available |
|---|---|
| Material: | Organic Silicone |
| Application: | Industrial, Molded Products |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
Payment Guarantee
Platform-protected payments with refund support for eligible order issues.
Platform Logistics
Inspection Service
After-Sales & Dispute Handling
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
(IOTA- MF260 series)
Description:
IOTA MF260 is a silicone compound that is formed by thermal vulcanization after adding a vulcanizing agent (the vulcanizing agent is selected according to the process requirements).
Advantages: 1. Easy to process
2. Good mechanical properties, high strength and resilience
3. Excellent oil resistance, solvent resistance and high and low temperature resistance, low dielectric loss of transformer oil
Product technical data:
|
ITEM |
index |
|
|
serial number |
IOTA-MF260 |
|
|
Test Methods |
Appearance |
|
|
/ |
translucent |
|
|
density/ g/cm3 |
ASTM D792 |
1.43 |
|
hardness/shoreA |
ASTM D2240 |
60 |
|
Tensile Strength/MPa |
ASTM D412 |
9.1 |
|
Elongation at break/% |
ASTM D412 |
370 |
|
Tear strength/KN/m |
ASTM D624-B |
19 |
|
compression permanent deformation(177ºC*22h ) |
ASTM D395 |
20 |
|
Resilience/% |
ASTM D1054 |
26 |
|
*heat resistance 200ºC×72h |
Hardness change (Shore A) |
+3 |
|
Tensile strength change rate,% |
-20 |
|
|
Elongation at break,% |
-21 |
|
|
Fuel C volume change rate/%25ºC/72h |
ASTM D471 |
+20 |
|
vulcanization conditions |
Add 0.7 parts of double 25, first-stage vulcanization: 170ºC×15min, second-stage vulcanization: 200ºC×4h |
|
*The data in the table are typical product performance and do not serve as factory standards.
*Meeting heat resistance requirements requires the addition of heat-resistant additives
Processing suggestions:
It is recommended to use 0.6 to 1 part of bis-penta-sulfide curing agent (2,5-dimethyl-2,5-bis(tert-butylperoxy)).
Customers should determine the most appropriate vulcanization temperature and time based on product size and vulcanization method.
Application:
Can be used for molded products, injection molding and extruded tube forming products; has good mechanical properties
Product packaging: 20Kg per box
Storage period:
IOTA MF260 should be stored in unopened original packaging below 40ºC for 12 months from the date of production.