| Appearance: | Liquid |
|---|---|
| Usage: | Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals |
| Working Time(Mins): | 35-45 |
| Curing Time(Hrs): | 4-6 |
| Hardness(Shore a): | 40±5 |
| Thermal Conductivity(W/M·K): | ≥0.8 |
| Samples: |
|---|
Suppliers with verified business licenses
Audited Supplier IOTA Silicone Encapsulating Rubber 13 series (Addition Cured)
Product Introduction
Potting silicone is a pourable addition curing RTV-2 silicone rubber for coating,lamination,encapsulation and molding purposes.It will protect components against shock, vibration,moisture,ozone,dust,chemicals and other environmental hazards.
Application
Used in protecting of electronic components and other assemblies.
Properties
Low viscosity.
High and low temperature resistant.
Fire and water proof.
Anti-shock and anti-oxidation.
Parameter:
|
|
1301 |
1302 |
1303 |
1300 |
|
Color |
White |
Black |
Grey |
Transparent |
|
Density(g/cm3) |
1.4 |
1.4 |
1.4 |
0.98 |
|
viscosity(mPa.s) |
2000±500 |
2000±500 |
2000±500 |
1000-1500 |
|
Mixing ratio |
1:1 |
1:1 |
1:1 |
1:1 |
|
Working time(mins) |
35-45 |
35-45 |
35-45 |
50-60 |
|
Curing time(hrs) |
4-6 |
4-6 |
4-6 |
8-10 |
|
Hardness(Shore A) |
40±5 |
40±5 |
40±5 |
25-30 |
|
Adhesive |
No |
No |
No |
No |
|
Thermal conductivity(W/m·K) |
≥0.8 |
≥0.8 |
≥0.8 |
≥0.3 |
|
Volume resistivity(Ω.cm) |
≥1014 |
≥1014 |
≥1014 |
≥1014 |
|
Breakdown voltage(KV/mm) |
≥20 |
≥20 |
≥20 |
≥20 |
|
Dielectric constant(50 HZ) |
2.7~3.3 |
2.7~3.3 |
2.7~3.3 |
2.7~3.3 |
|
Dielectric loss(20 HZ) |
≤0.02 |
≤0.02 |
≤0.02 |
≤0.02 |
|
Operating temperature(°C) |
-50~250 |
-50~250 |
-50~250 |
-50~250 |
|
Flammability rating |
UL94-V0 |
UL94-V0 |
UL94-V1 |
UL94-HB |
|
Waterproof level |
IPX6 |
IPX6 |
IPX6 |
IPX4 |
The above data are tested and obtained in a strict laboratory (25°C).
Cure inhibition
Silicone rubber compound will cure in contact with most clean, dry surfaces. However, certain materials,such as butyl and chlorinated rubber, materials containing sulfur, amines, and non-platinum RTV silicone rubber compounds will cause cure inhibition and rubber will not cure.If compatibility between the rubber and the surface is in question, a small scale test is recommended.
How to use
Mixing
Dispensing required amounts of Parts A and B into mixing container (1A:1B by volume or weight), making sure that you scrape the sides and bottom of the mixing container several times. After mixing parts A and B, vacuum degassing is recommended to eliminate any entrapped air in liquid silicone rubber.
Pouring
For best results, pour your mixture in a single spot at the lowest point of the containment field. Let the rubber seek its own level. A uniform flow will help minimize entrapped air.It is recommended to use an automatic glue filling machine, and the silicone rubber does not generate air bubbles during the stirring and filling process.
Curing
Silicone will cure to a flexible rubber within 24 hours at room temperature (22°C-25°C) and the mold can then be separated from the original. High temperature cures fast,low temperature cures slowly.The best bonding performance of the adhesive silicone can be achieved after the silicone has been cured for 72 hours.
Storage
When stored at or below 30°C in the original unopened containers, this product has a usable life of 12 months from the date of production. Storing material at warmer temperatures will also reduce the usable shelf life of unused material.Silicone rubber will precipitate during long-term storage, and the precipitate is a flame retardant and thermally conductive material. It is used after stirring evenly without affecting the use and quality.
Packing
This product is available in 1kg, 3kg, 5kg, 10kg, 20kg, 25kg, 200kg