UV Cure High Transparent Liquid Silicone Rubber Iota 3530-Ab for Optical Components with High Transparency/Swimming Goggles/LED Lampshades

• Raw Material: Synthetic Rubber
• Material: Silicone Rubber
• Appearance: Liquid
• Model NO.: UV cure high transparent liquid silicone rubber IO
• Form: Liquid Rubber
• Trademark: IOTA
• Origin: Bengbu Anhui China
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

UV cure high transparent liquid silicone rubber IOTA 3530-AB

Description
IOTA 3530-AB is a new UV curing material that has a faster curing rate when injected at room temperature. It also has excellent mechanical properties.

features:

1. l Cure as needed
2. l Fast UV curing at low temperature
3. l for general purpose UV curing systems
4. l Excellent transparency
5. l good liquidity
6. l Good thermal stability
7. l has high stability at low temperatures

Application
Optical components with high transparency, swimming goggles, LED lampshades, etc

Usage
1. Use ratio A:B=1:10
2. The rubber material is injected into the mold by the injection machine, and the rubber material must be full. (Can also be poured into the mold molding).
3. Recommended curing conditions :800mj/cm² irradiation for 5s or other irradiation conditions.
4. The specific conditions of molding can be determined according to the thickness or size of the product.
 

status	item	unit	result
Before curing	Component		Two components
	Curing method		UV curing
	colour		Colorless and transparent
	A Viscosity 29#	Pa.s	1000
	B viscosity 29#	Pa.s	3500
Curing condition	A:B=1:10, with 800mj/cm2 intensity of ultraviolet irradiation for 5s
After curing	Hardness	Shore A	53
	Specific gravity	g/cm³	1.02
	Tensile strength	MPa	6.2
	Elongation at break	%	102

Storage
Store sealed in a cool, dry and ventilated place.
Ambient temperature The temperature is lower than 25 ° C.
Agent A needs to be stored away from light.


Shelf life
6 months

Packing
20KG/ barrel 200KG/ barrel

Attention
1. The higher the temperature, the shorter the storage time, try to store at low temperature.
2, when used, avoid contact with compounds containing elements such as N, S, P and Sa, otherwise it will cause non-vulcanization or incomplete vulcanization:
3. The catalyst should be stored away from light.