| Appearance: | Liquid |
|---|---|
| Usage: | Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals |
| Solvent: | Butyl Ether |
| Solid Content: | 20% |
| Liquid Density: | 1.16-1.31 G / Ml |
| Density After Curing: | 1.6-2.0 G / Ml |
| Samples: |
|---|
Suppliers with verified business licenses
Audited Supplier Perhydropolysilazane (PHPS) or Inorganic Polysilazane IOTA-PHPS
Description:
The coating product is mainly composed of perhydropolysilazane IOTA PHPS,diluted and stored in a solvent.
Name: Hydrophilic Super Hard Stain Resistant Nano-Coating Materials
English synonyms: PHPS
Polysilazane Liquid Coating Materials
Features:
Good adhesion on the metal ceramic polymer materials
Can be converted to SiO2 at a lower temperature
Short curing time
Curing a variety of ways
Good solubility
Technical Parameters:
Appearance: colorless transparent liquid
Solid content: 20%
Solvent: butyl ether
Liquid density: 1.16-1.31 g / ml
Density after curing: 1.6-2.0 g / ml
Curing mechanism:
The curing of the coating material mainly is the Si-N bond hydrolysis, the mechanism is as follows:
Curing conditions:
Room temperature: more than 7 days
Moisture curing: humidity 90%, temperature 150 ºC, 2h
Coating properties:
Coating thickness (nm): >100
Composition: SiOx
Hardness (GPa): 3 (ammonie curable)
8-10 (high temperature curing)
Elastic modulus (GPa): 60 (NH3.H2O curing)
100-130 (high temperature curing)
Pencil Hardness: 9H(Chinese)
6H (Mitsubishi)
Adhesion (grid method): 0 level
Transparency (visible light): > 90%
Temperature resistance (air): 800 ºC
Acid (10% hydrochloric acide): about a month.
Rust, alkali, salt water resistance
Applications:
Building anti - graffiti
electronic circuit
Semiconductor insulating layer
Metal high temperature oxidation resistance
Plastic packaging waterproof gas barrier
Metal anti-corrosion
Surface hardening coating
How to use:
First, clean the substrate surface, coating products using spin-coating, rubbing, spraying, dipping, etc. construction, and then by room temperature curing, high temperature curing, etc. curing.
Clean:
Proper cleaning is important. After using promptly use aceton or solvent oil to wipe the tool cleaning.IOTA PHPS cured, the solvent can not be washed away.
Product packaging:
According to customer demand, 0.5-10 liters metal sealed drum, generally use xylene, dibutyle ether or dichloromethan for filling, solid content of 2-20%.
Storage:
Shelf life: 2years; after the application, it depend on the protective measures, sealed low temperature drying case, the applicable period of more than half a year.
Precautions:
Should l be in a ventilated, dry environment, and the use of necessary protective measures, such as gloves, masks, goggles; shall not
Do not place uncured IOTA PHPS near to fire, humid air, or water.
After opening, seal it in a timely manner. If it is used in a humid environment, replace the container with nitrogen after using.