Transulcent Fluorosilicone Base Iota M1200 Low Fluorine Content Has Wide Application Temperature Range

• Appearance: Liquid
• Usage: Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
• Color: Translucent
• Model NO.: IOTA M1200
• Transport Package: Plastic Bags
• Specification: 12.5kg per sack, 2 sacks in 1 carton
• Trademark: IOTA
• Origin: Anhui, China
• HS Code: 3910000000

Product Description

Fluorosilicone Base IOTA M1200 Low Fluorine Content
 

Composition

Uncatalyzed fluorosilicone rubber based on fluorosilicone gun,and mixed evenly with some kinds of fillers and additives

Characteristics

IOTA-R-M1200 is translucent fluorosilicone base. It has integrated advantages that both the silicone rubber and fluoro rubber have.

1. Wide application temperature range (-65C~200ºC), better low-temperature resistance than that of normal IOTA-R- M1000;

2.Similar resistance to solvent &fuel oil to that of fluororubber;

3.Keeping high tensile force retention at high temperature which is like silicone rubber;

4.High insulation;

5.High selective permeability meets requirements of environmental protection.

Therefore it can be used as seal material in special condition with requirement of resistance to high and/or low temperature,oil and some solvents.
 

Items	Testing method	Index
		M1230	M1240	M1250	M1260	M1270	M1280
Appearance	Eyeballing	translucent,smooth surface,without visible impuritie
Hardness (Shore A)	ASTM D2240	30±5	40±5	50±5	60+	70±5	80±5
Tensile Strength (MPa)Die C	ASTM D412	≥6	≥8	≥8	≥8	≥7	≥6
Elongation at Break (%)Die C	ASTM D412	≥350	≥350	≥300	≥250	≥200	≥150
Tear Strength (KN/m)Die B	ASTM D624	≥20	≥20	≥20	≥20	≥15	≥15
Compression Set 177ºC 22hr (25%)B type	ASTM D395	≤25	≤25	≤25	≤25	≤25	≤25
Volume Change (reference fuel B)(%)(23ºC×70hr)	ASTM D471	≤130	≤130	≤130	≤130	≤130	≤130

Properties obtained using 1.5 phr DCBP. Molded 15min at 110 ºC, post-cured 4hr at 200ºC. If other cure temperature needed,vulcanization system shall be changed.
 

Application
1.Aviation industry: seals in aircraft to resist to fuels and/ or lubricants, such as O-rings,spacers, integral tank sealing, sensor material,diaphragms and clips for spacers.
2.Auto industry:used as sealing rings,grease seals,diaphragms,pipes and valve-linings for various types of vehicles.
3.Petrochemistry industry:sealing parts used in pump,valve and oil tank,which are used under high/low temperature and chemical circumstance.
4.Medical and health care:used in manufacturing medical apparatus or instruments,artificial visceral organs,such as medical pipes,medical hoses for fluids and artificial valves.
5.Military industry:used in poor condition of environment,which requires material to resist to low temperature,oil and acid,for instance,corrugated pipes used in hydraulic system of military aircraft,sealing rods for doors,windows and covers on special vehicles,sensor material and etc.

 

Package 
Plastic bags,12.5kg per sack,2 sacks in 1 carton.
 

Storage 
Shall be stored in dry and ventilated places at room temperature (25ºC).Validity is 1 year.

Transportation 
Transport it as non-dangerous cargo.

Attention
1.The product shall be kept neutral,avoid being contacted with acid,alkaline substance.

2.The product can flow under its own weight. Keep it in good condition of packing during transportation and application in order it not to flow out.