Description
IOTA 9283 is a liquid polysilazane with Si-N structural, mainly function group is Me and modified fluorine groups. It is developed for room temperature cured hydrophobic coating systems. The product has a unique Si-NH-Si bond, can be cured at room temperature, curing mainly involved in the reaction of Si-NH-Si hydrolysis and oxidation. While the Si-NH-Si bond and the substrate surface-OH easily react, and bring the good adhesion to substrate. Add appropriate catalyst in the resin can promote Si-H and Si-NH-Si reaction, after curing resin can generate three-dimensional cross-linked structure, giving the material good mechanical properties.
IOTA 9283 has excellent hydrophobic property as contain fluorine group, keep the colorless transparent coating with good transmittance more than 95%.
IOTA 9283 has low viscosity and good adhesion, can be applied to various types of substrates by smearing, dipping, spraying, brushing and other methods, the main substrates are metals, alloys, glass, paint films and plastics (such as PP, PC, PVC, PMMA), etc.
Product Features
Low viscosity
Excellent Hydrophobic coating
Short surface dry time
Various curing methods
Non-flammable after curing
Anti-oxidation, anti-corrosion
Easy to clean
Good adhesion on the metal ceramic graphite materials
Applications
Coatings
Adhesives
Non-flammable composites
Polymer matrix composites
Glass and Abrasives
Applications with low surface tension and high hydrophobic
Technical index
| Appearance: | Colorless to light yellow transparent liquid |
| Molecular weight (Mn): | 900-1000 |
| Solid content: | 10% (other contents could be customized) |
| Liquid Density: | 0.68g/cm3 |
| Viscosity: | 2cp-5cp |
| Cracking threshold: | 100µm+(coating thickness) |
| Curing conditions: | cured in room temperature without catalyst |
| Surface dry time in room temp.: | 10min-15min |
Totally cured time:
a. more than 24hours in room temp.
b. Heating could promote the curing process, heat in 120ºC- 150ºC for 2-5hours after surface dry.
The hardness after cured:
Room temp. cured for 12hours: 4H
Room temp. cured for 24hours: 6H
Hydrophobic angle: 110°-120°
Recommended temperature of varnish coating: <300ºC
Recommended operating temperature with main coating: <1000ºC
Chemical masking: perform good with O2,H2O and other gas
Linear shrinkage: <1%
Transmittance (visible light): >95%
Metal Adhesion (Cross-Hatch): 0 grade
Shelf life: 12months in unopened condition
Notes
Solid content of IOTA 9283 is 10%, could be customized as customers' requirements.
The heating curing process of IOTA 9283 is operated after surface dried, curing temp. is 60ºC-200ºC. The totally cured time will be shorten as the temp. increasing.
The hydrophobic angle of cured IOTA 9283 coating is stable at 115°, it could keep around 109° after heating with 350ºC in 1hour.
The operating temp. of IOTA 9283 is related to the coating thickness, the higher thickness, the better protection, but the coating is easy to be crack in high. Temp.
Compatibility
The product could be miscible with most non-polar solvents, such as alkanes, ethers, ketones, esters. Insoluble in alcohol and ether solvents, such as diethylene glycol dimethyl ether, diethylene glycol dibutyl ether, tetraethyl ether Butyl glycol ether.
It's also miscible with a variety of resins, such as epoxy silicone resin, silicone resin, it will shorten the curing time and improve resin hardness when mixed with silicone resins.
Operation methods
Operating and storing in a dry, cool and well-ventilated environment, away from heat and fire sources, the recommended temperature is 0-20ºC.
The gloves, masks, etc. is necessary when taking the product.
Uncured product should not be placed close to fire sources, humid air, or water.
The container must be replace the air with nitrogen/argon and completely sealed in time after use.
Unused product that has been formulated cannot be recycled and should be disposed of in accordance with local regulations.
Products beyond the shelf life can be used only after the retesting complied.
Package
Packed in 100ml, 1L, 5L metal drums.
Precautions
The storage environment should be dry, cool and well ventilated, away from heat and fire sources. The packaging container must be kept tightly closed and handled with care. The storage temperature should be kept between 0°C and 20°C, and the storage period is 12 months.
Clean
Proper cleaning methods are important, quickly wipe down the surface with acetone or mineral spirits after use.
Once IOTA 9283 is cured, the coating cannot be washed away by solvent