Food Grade Iota M4240hg a/B Liquid Silicone Rubber for Baby Care, Food Contact, Seal Ring, Other Injection Products

• Material: Organic Silicone
• Application: Household, Medical, Industrial, Agricultural
• Certification: FDA, REACH, RoHS
• Transport Package: Component a: 200 Kg/Drum, Component B: 200 Kg/Drum
• Specification: Component A: 200 Kg/drum, component B: 200 Kg/drum
• Trademark: iota
• Model NO.: Liquid Silicone Rubber for baby Nipple IOTA M4240H
• Origin: Bengbu Anhui China
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

Liquid Silicone Rubber for baby Nipple IOTA M4240HG A/B

 

Description:

IOTA M4240HG A/B is a food grade liquid silicone rubber product.

 

Features:

1. Two-component, 1:1 mix ratio

2. Excellent mold release

3. Fast heat curing

4. Excellent mechanical properties

5. Compliant with BfR, FDA, ROHS

 

Application:

1. Baby care

2. Food Contact

3. Seal ring

4. Other injection products, etc.

 

Curing:

temperature	Curing time, 2mm thickness
130ºC	90 S
150ºC	45 S

 

Technical data:

Properties	Test method	value
Uncured products
Component A
color		transparent
Density 23ºC		1.12 g/cm^3
Viscosity (23ºC,10S^-1)	ISO3219	300 Pa.s
Component B
color		transparent
Density 23ºC		1.12 g/cm^3
Viscosity 23ºC, 10S^-1	ISO3219	290Pa.s
Technical data(A/B mixed)
Mixing ratio (weight)	A:B	1:1
Viscosity 23ºC, 10S^-1	ISO3219	300Pa.s
curing time		see curing conditions
Technical data(cured)	(125±2ºC, 5min)
color		transparent
Density 23ºC	ISO2781	1.12 g/cm^3
Hardness	DIN 53505	40
Tensile Strength	DIN 53504	9 MPa
Elongation	DIN 53504	550 %
tear strength	ASTMD 624B	33 KN/m

All values are unique and should not be accepted as standard specifications.

 

NOTES

1. M4240HG A/B is a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.

2. Only same batch of components A and B could be mixed together.

3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.