Iota-5220A/B UV Curing Loca

• Material: Organic Silicone
• Application: Household, Medical, Industrial
• Certification: SGS
• Purity: 99.8%
• Transport Package: 200kg/Drum, 25kg/Drum
• Specification: Iron Bucket
• Model NO.: IOTA-5220A/B
• Trademark: IOTA
• Origin: China
• HS Code: 39100000
• Production Capacity: 300ton/Month

Product Description

UV curing LOCA IOTA-5220A/B

Description
The product is a two-component uv curing liquid silicone gel. It has excellent yellowing resistance, aging resistance and low shrinkage properties. It is mainly applied to full bonding of touch screen display and LCD as well as car monitor.

Typical properties

Item	Method	Value
Before mix A &B
Appearance	Visual	A. Colorless liquid B. Colorless liquid
Glue viscosity	ISO3219	A. 2200Mpa.s B. 1000Mpa.s
Mix viscosity (mpa.s)	ISO3219	2200Mpa·s
Density(g/cm3)	GB/T4472-2011	0.97 g/ml
After mixing A & B but before curing
Mix ratio		10:1
Operating time(min ,25ºC)	25ºC Avoid light	48h
Curing condition		UV-LED(365nm)3000mj/cm 2 +60ºC /30min
After curing
Appearance	Visual	Colorless transparent gel
Yellowing index	ASTM E313-15el, film thickness 1mm	<0.1
Luminousness(400nm)	UV spectrophotometer, Film thickness1mm	99%
Haze	GB/T 2410-2008, film thickness 1mm	<0.1%
Needle penetration	DIN ISO 2137	95  1/10mm
Relative defining constant	IEC 60250	2.85
Refractive index	nd 25	1.407
Thermal conductivity	GB/T 10297-1998	0.2W/m.k
Volume shrinkage(%)	GB/T 24148.9-2014	<0.1%
Surface tension	GB/T 2237-2008	24.0mN.m-1
G+G bonding power Mpa	Cross drawing force, film thickness 0.5mm	0.5mpa

Surface treatment
All interfaces contacts with the glue must be cleaned and stored to ensure that there is no phosphorus (P), sulfur (S), nitrogen (N), organic tin (Sn), water, polyurethane and other catalyst toxic substances, so as not to cause curing obstacles and deterioration

Mix procedure
Formula of component A is cross linker and B contains platinum catalyst. The platinum catalyst can make the component to do crosslinking reaction. So please avoid mixing A and B while you are using the operating tools

Curing
The curing of the glue is closed relate to the curing time, temperature as well as glue thickness. Mix ratio of A and B is 10:1. The proportion deviation has a certain effect on the hardness of glue, you can add addition of group A to improve the hardness

 

Package
A 5kg/barrel B 0.5kg/barrel

Storage
1. Sealed store at cool dry ventilated places in original container
2. Room temperature (15-35ºC) 

Shelf life
6 months from production date

Handling precautions
1. Please test the matching performance between the glue and LCM&TP before bonding
2. Please keep 7 days at temperature of 25ºC after curing for quality testing.