Post Cured Free Liquid Silicone Rubber Iota M6030 for Baby Car Efood Contact Sealing Ringother Injection Products

• Appearance: Liquid
• Usage: Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
• Color: Transparent
• Viscosity 23ºC 0s-1: ISO3219
• Density at 23ºC: 1.11 g/cm3
• Mix Ratio: a:B1:1
• Model NO.: Post cured free liquid silicone rubber IOTA M6030
• Technical Data: 125±2ºC*300 S
• Transport Package: Component a: 200 Kg/Drum, Component B: 200 Kg/Drum
• Specification: Component A: 200 Kg/drum, component B: 200 Kg/drum
• Trademark: iota
• Origin: Bengbu Anhui China
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

Post cured free liquid silicone rubber IOTA M6030

Description

IOTA M6030 A/B is a liquid silicone rubber free of post cured.

 

Features:

Two component, 1:1 mixing ratio  

Excellent mold release

VOC < 0.5%

Rapid heat curing

Excellent mechanical properties

Meet standard of BFR, FDA and RoHS

 

Application:

Baby care

Food contact

Sealing ring

Other injection products, etc

 

Curing condition

Temperature	Curing time:2mm thickness
130ºC	90 S
150ºC	45 S

 

NOTES

1.IOTA M6030 A/B a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning.

2. Only same batch of components A and B could be mixed together.

3. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers.

 

Packing and storage

Component A:200kg/drum, component B: 200kg/drum

Store under 23ºC to avoid exposure to rain and sunlight.

Shelf life: 12 months, unopened condition.

 

Technical index:

Properties	Test method	Value
Uncured
Component A
Color		Transparent
Density at 23ºC		1.11 g/cm^3
Viscosity 23ºC,10S^-1	ISO3219	280 Pa.s
Component B
Color		Transparent
Density at 23ºC		1.11 g/cm^3
Viscosity 23ºC,10S^-1	ISO3219	250 Pa.s
Technical data(A/B mixed)
Mix ratio(weight)	A:B	1:1
Viscosity 23ºC,10S^-1	ISO3219	280 Pa.s
Curing time		See curing conditions
Technical data(cured)	125±2ºC*300 S
Color		Transparent
Density 23ºC	ISO2781	1.11g/cm^3
Hardness	DIN 53505	30
Tensile strength	DIN 53504	7.0 Mpa
Elongation at break	DIN 53504	600%