High Purity Hydrophilic Super Hard Nano Coating with Anti-Graffiti Anti-Corrosion Oxidation Resistance Perhydropolysilazane Phps

• After-sales Service: N/a
• Warranty: N/a
• Material: Silicone
• Model NO.: PHPS
• Color: Transparent
• Appearance: Liquid
• Method: Spray
• Level: Finish Coat
• Drying Method: Air Drying
• Certification: RoHS, ISO9001
• Substrate: Ceramic
• CAS No.: N/a
• Main Raw Material: Silicone
• Components: Siicone
• Applications: Building Anti - Graffiti
• Applications1: Metal Anti-Corrosion
• Applications2: Metal High Temperature Oxidation Resistance
• Applications3: Surface Hardening Coating
• Transport Package: 20kg/Drum 200kg/Drum
• Trademark: IOTA
• Origin: Cn
• Production Capacity: 3500

Product Description

Description:
The coating product is mainly composed of perhydropolysilazane MY PHPS, with a small amount of organic polysilazane, nano filler, curing accelerator and other functional additives, and is diluted and stored in a solvent.

Features:
Good solubility
Short curing time
Curing a variety of ways
Good adhesion on the metal \ ceramic \ polymer materials
Can be converted to SiO2 at a lower temperature

Applications:
Building anti - graffiti
Metal anti-corrosion
Rail
Semiconductor insulating layer
electronic circuit
Plastic packaging waterproof gas barrier
Metal high temperature oxidation resistance
Surface hardening coating

Product packaging:
According to customer demand, 0.5-10 liters metal sealed drum, generally use xylene, dibutyl ether or dichloromethane for filling, solid content of 2-20%.

How to use:
First, clean the substrate surface, coating products using spin-coating, rubbing, spraying, dipping, etc. construction, and then by room temperature curing, high temperature curing, etc. curing.

Clean:
Proper cleaning is important. After using promptly use acetone or solvent oil to wipe the tool cleaning.
MY PHPS cured, the solvent can not be washed away.

Storage:
Shelf life: 2years; after the application, it depend on the protective measures, sealed low temperature drying case, the
applicable period of more than half a year.

Precautions:
Should l be in a ventilated, dry environment, and the use of necessary protective measures, such as gloves, masks, goggles; shall not

Do not place uncured OPSZ-9150 near to fire, humid air, or water.
After opening, seal it in a timely manner. If it is used in a humid environment, replace the container with nitrogen after using.
 

Appearance	colorless transparent liquid
Solid content	20%
Solvent	butyl ether
Liquid density	1.16-1.31 g / ml
Density after curing	1.6-2.0 g / ml
Curing conditions:
Room temperature	more than 7 days
Moisture curing	humidity 90%, temperature 150 ºC, 2h
Coating properties:
Composition	SiOx
Coating thickness (nm)	>100
Hardness (GPa)	3 (ammonia curable)
	8-10 (high temperature curing)
Elastic modulus (GPa)	60 (NH3.H2O curing)
	100-130 (high temperature curing)
Pencil hardness	9H (Chinese)  6H (Mitsubishi)
Transparency (visible light)	> 90%
Adhesion (grid method)	0 level
Temperature resistance (air)	800 ºC
Rust, alkali, salt water resistance
Acid (10% hydrochloric acid)	about a month.