Iota Flsr8520 Fluorosilicone Coating

• Appearance: Liquid
• Usage: Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
• Color: Transparent
• Trademark: IOTA
• Origin: Bengbu Anhui China
• Model NO.: IOTA FLSR8520 fluorosilicone coating
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

IOTA FLSR8520 fluorosilicone coating

 

_Description:

IOTA FLSR8520 fluorosilicone coating is an adhesive-type liquid fluorosilicone material, has excellent adhesion, oil resistance, high and low temperature resistance, and hydrophobicity. It can be used for bonding and surface modification of various substrates, such as PET, PA, chemical fibers, fiberglass, leather, metals, etc. During use, organic solvents can be added for dilution, imparting excellent surface properties to the material after immersion or spraying. 

 

Product performance: 

Item	Test Methods	IOTA FLSR8520
Component A color	Visual inspection	translucent
Component B color	Visual inspection	translucent
The mixing ratio	Q/371002WXH015-2017	1:1
Mixed viscosity/mPa.s (25ºC)	Q/371002WXH015-2017	50~5000
Operating time/h(25ºC)	Q/371002WXH015-2017	2~4
Solid content/%	Q/371002WXH015-2017	30~70
density/g/cm3	ASTM* D792	1.02~1.40
hardness/Shore A	ASTM D2240	22
Tensile Strength/MPa	ASTM D412	3.0
Elongation at break/%	ASTM D412	265
Tear strength/kN/m	ASTM D624-B	10.2
Shear strength(PET)	GB/T 7124	100% cohesive destruction

 

Usage:

IOTA FLSR8520 fluorosilicone coating is packaged in two components. When in use, components A and B can be mixed in a 1:1 weight ratio by mass and applied directly. Alternatively, according to process requirements, an appropriate amount of organic solvent can be added to the material for dilution before application. 

 

Packaging:

Packed in 10kg plastic drums.

 

Shelf Life: 

Store in a cool, dry environment in, shelf life is 6 monthes in unopened original packaging.

 

Precautions:

Avoid contact with compounds containing nitrogen, sulfur, phosphorus, and heavy metals to prevent incomplete vulcanization or non-vulcanization of the product.