STS is an escrow service that protects both buyers and suppliers. Funds are held securely by Made-in-China.com until order terms (e.g., delivery, quality) are fulfilled
|
Still deciding? Get samples of $ !
Request Sample
|
| Customization: | Available |
|---|---|
| Material: | Organic Silicone |
| Application: | Industrial |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
Payment Guarantee
Platform-protected payments with refund support for eligible order issues.
Platform Logistics
Inspection Service
After-Sales & Dispute Handling
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Product Introduction:
IOTA LSR 3061 A/B is a liquid silicone rubber with self-adhesive properties towards PC (Polycarbonate), while also exhibiting good mold release characteristics.
Main Features:
Two-component, 1:1 mixing ratio
Excellent mold release
Outstanding self-adhesion to PC
Fast thermal curing
Excellent mechanical properties
Typical Applications:
Swimming goggle sealing
Phone case overmolding
Smartwatch back cover sealing ring
Phone SIM tray sealing
Important Notes:
IOTA LSR 3061 A/B is a product cured using a platinum catalyst. The platinum catalyst is in Component A. Strict attention must be paid during use to avoid catalyst poisoning.
Only Component A and Component B from the same batch number should be mixed and used together.
To ensure optimal fluidity and homogeneity, the material must be stirred thoroughly before being transferred to containers to uniformly disperse any fillers that may have settled during storage.
Technical Parameters:
|
Property |
Test Method |
Value |
|
Uncured Product |
|
|
|
Component A |
|
|
|
Viscosity 23°C, stirred |
ISO3219 |
300 Pa·s |
|
Component B |
|
|
|
Viscosity 23°C, stirred |
ISO3219 |
500 Pa·s |
|
Product Data (A+B Mixed) |
|
|
|
Mixing Ratio (by weight) |
A:B |
1:1 |
|
Viscosity 23°C, stirred |
ISO3219 |
400 Pa·s |
|
Pot life at Room Temp. |
23±2°C |
2 h |
|
Curing Time |
|
Refer to Curing Conditions |
|
Product Data (Cured) |
(Cured 24h at 23±2°C) |
|
|
Density 23°C |
ISO 2781 |
1.14 g/cm³ |
|
Hardness (Shore A) |
DIN 53505 |
60 |
|
Tensile Strength |
DIN 53504 |
≥10.0 MPa |
|
Elongation at Break |
DIN 53504 |
≥450 % |
|
Tear Strength |
|
≥40 KN/m |
Packaging Information:
Component A: 200 kg/drum, Component B: 200 kg/drum
Storage and Shelf Life:
When stored unopened below 23°C, the shelf life is 12 months. The best use-by date is marked on the label of each product's external packaging.
Material exceeding the shelf life is not necessarily unusable. In such cases, performance tests for relevant parameters must be conducted to ensure quality.