Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing

Product Details
Appearance: Liquid
Usage: Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
Color: Translucent
Still deciding? Get samples of US$ 50/kg
Request Sample
Diamond Member Since 2021

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

Registered Capital
10000000 RMB
Plant Area
1001~2000 square meters
  • Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing
  • Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing
  • Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing
  • Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing
  • Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing
  • Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing
Find Similar Products

Basic Info.

Model NO.
IOTA R1000
Transport Package
Plastic Bags
Specification
12.5kg per sack, 2 sacks in 1 carton
Trademark
IOTA
Origin
Anhui, China
HS Code
3910000000

Product Description

Fluorosilicone Base IOTA R1000 High Rebound Resilience
 

Composition

Uncatalyzed fluorosilicone rubber based on fluorosilicone gum,and mixed evenly with some kinds of fillers


Characteristics

IOTA-R-R1000 is translucent fluorosilicone base.It has integrated advantages that both the silicone rubber and fluororubber have.

1. It has better rebound resilience than normal ones of IOTA AFS-R-M1000;

2. Wide application temperature range(- 60ºC~200ºC);

3. Similar resistance to solvent &fuel oil to that of fluororubber;

4. Keeping high tensile force retention at high temperature which is like silicone rubber;

5. High insulation;

6.High selective permeability meets requirements of environmental protection.

Therefore it can be used as seal material in special condition with requirement of resistance to high and/or low temperature,oil and some other chemical mediums.

Items

Testing

method

Index

R1040

R1050

R1060

R1070

R1080

Appearance

Eyeballing

translucent,smooth surface,without visible

Hardness (Shore A)

ASTM D2240

40±5

50±5

60±5

70±5

80±5

Specific Gravity (g/cm²)

ASTM D792

1.41

1.43

1.45

1.48

1.52

Tensile Strength (MPa)Die C

ASTM D412

≥9

≥9

≥9

≥8

≥7

Elongation at Break (%)Die C

ASTM D412

≥350

≥300

≥250

≥200

≥150

Tear Strength (KN/m)Die B

ASTM D624

≥20

≥20

≥20

≥15

≥15

Compression Set 177ºC 22hr(25%)B type

ASTM D395

≤15

≤15

≤15

≤15

≤15

Veitical Rebound Resilience (%)

ASTM D2632

25

25

25

25

25

Volume Change (reference fuel B)(%)(23ºC×70hr)

ASTM D471

≤20

≤20

≤20

≤20

≤20

Propeities obtained using 0.53phr DBPH. olded 10min at 170ºC, post-cured 4hr at 200ºC. If other cure temperature needed,vulcanization system shall be changed.

Application

1. This is a kind of material with high rebound resilience,suitable for higher requirement in application. 

2.Suitable for faster curing.

3.Can be applied in aviation industry,auto industry,petroleum chemical industry,medical and health care industry and military industry.


Package 
Plastic bags,12.5kg per sack,2 sacks in 1 carton.

 

Storage 
Shall be stored in dry and ventilated places at room temperature (25ºC).Validity is 1 year.


Transportation 
Transport it as non-dangerous cargo.


Attention
1.The product shall be kept neutral,avoid being contacted with acid,alkaline substance.

2.The product can flow under its own weight.Keep it in good condition of packing during transportation and application in order it not to flow out.

Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing

 

Translucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster CuringTranslucent Fluorosilicone Base Iota R1000 High Rebound Resilience Is Suitable for Faster Curing

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier