Common Grade Htv Silicone Rubber Used in Good Processability Used in Keypads/ Sealing Rings and Sealing Gaskets

• Appearance: Liquid
• Usage: Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
• Color: White
• D7125: 25±3
• D7130: 30±3
• D7140: 40±3
• Model NO.: Common grade HTV silicone rubber
• D7150: 50±3
• Transport Package: 20kg/ Carton Lined with Plastic Bags or Sheets.
• Specification: 20kg/ carton lined with plastic bags or sheets.
• Trademark: IOTA
• Origin: Bengbu Anhui China
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

Common grade HTV silicone rubber

This product has good physical and mechanical properties and processability. This product can be divided into two sub-categories: rubber for molding and rubber for extrusion. The rubber for molding is vulcanized with 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane as vulcanizator, applicable to manufacturing of industrial miscellaneous parts such as keypads, sealing rings and sealing gaskets; and the rubber for extrusion is vulcanized with vulcanizator DCBP (Di-(2,4-dichlorobenzoyl) Peroxide), applicable to manufacturing of various electric wires, cables, hoses and tapes.

 

      Typical Properties:

 

Category	Item	Appearance	Hardness Shore A	Tensile strength MPa≥	Elongation at break %≥	Breaking set %≤	Tear strength B KN/m≥	Specific density 25°C g/cm³	Compression set 180*22h %≤	Resilience %≥
For molding	IOTA D7125	Ivory light yellow	25±3	3.5	700	8	10	1.05±0.05	-	-
	IOTA D7130		30±3	5.0	450	7	15	1.08±0.05	35	65
	IOTA D7140		40±3	6.5	400	7	16	1.13±0.05	30	60
	IOTA D7150		50±3	7.5	320	8	18	1.15±0.05	30	60
	IOTA D7160		60±3	7.5	280	8	18	1.19±0.05	30	50
	IOTA D7170		70±3	7.0	200	7	17	1.22±0.05	30	45
	IOTA D7180		80±3	7.0	150	6	16	1.25±0.05	25	45
	IOTA D7190		86±2	4.0	80	6	10	1.26±0.05	25	40

Physical data in the above table is for reference only.

Vulcanization condition: 175ºC× 5Min.

 Ratio of curing agent 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane:0.65%.

 

Advantage:

- Good processability

- Stable comprehensive physical properties

 

Applications:

- General industrial and civil silicone rubber products

 

Category	Item	Appearance	Hardness Shore A	Tensile strength MPa≥	Elongation at break %≥	Breaking set %≤	Tear strength B KN/m≥	Specific density 25°C g/cm³	Dielectric strength kV/mm ≥	Volume resistivity .cm≥
For extrusion	IOTA D7240	Ivory light yellow light gray	40±2	6.5	450	14	16	1.13±0.05	18	1.0 x 10¹4
	IOTA D7250		50±3	7.5	450	14	18	1.18±0.05	18	1.0 x 10¹4
	IOTA D7260		60±3	7.5	360	14	20	1.20±0.05	18	1.0 x 10¹4
	IOTA D7270		70±3	7.0	250	14	20	1.22±0.05	18	1.0 x 10¹4
	IOTA D7280		80±3	6.5	150	10	18	1.25±0.05	18	1.0 x 10¹4

 

Physical data in the above table is for reference only.

Vulcanization condition: 175ºC× 5Min.

 Ratio of curing agent:DCBP (Di-(2,4-dichlorobenzoyl) Peroxide) 0.65%.

 

Advantage:

- Common grade for extrusion

- Flexible processability

- Flexible comprehensive physical properties

 

Applications:

- General industrial pigmented wires and cables

 

Packing & Storage:

- 20kg/ carton lined with plastic bags or sheets.

- The products have a shelf life of 9 months from date of manufacture depending on the shore hardness if stored at room temperature in the originally sealed container.