Iota 1054 Chemicals Silicone Resin for Domestic Electrical Appliances

• Type: Synthesis Material Intermediates
• Appearance: Liquid
• Quality: Industrial
• Colour: Light Yellow
• Solid Content%: 48-62
• Viscosity S/T-4,25ºC: 20-250
• Model NO.: IOTA 1054 series
• Curing Time 270 Degree Celsius,Min.: 5-8
• Certification: SGS
• Transport Package: Galvanized Iron Sheet Barrel
• Specification: 25kg/50kg/200kg
• Trademark: IOTA
• Origin: China
• HS Code: 3910000000
• Production Capacity: 500mt/Month

Product Description

Details

Silicone resin for domestic electrical appliances

Product Item	Index						Features	Main application
	Appearance	Solid content%	Viscosity  s/T-4,25ºC	Surface drying time  room temperature	Curing time  270ºC, min.	Solvent
IOTA 1054-1	light yellow transparent ropy liquid	50±2	20-40	≤1	2h/180ºC	arene	fire-resistant, high hardness, high adhesive force	gas burner
IOTA 1054-2		60±2	>200	<2	5-8	esters	fire-resistant, high luster, high hardness(3H)	inner/outer coating
IOTA 1054-3		60±2	>150	<2	5-8	esters	fire-resistant, high luster, high hardness(3H)	inner/outer coating
IOTA 1054-4		60±2	>100	<2	5-8	esters	high luster, impact resistant, high adhesive force	high-temp. and color outer coating
IOTA 1054-5		60±2	>250	<2	5-8	esters	fire-resistant, high hardness(>3H), high luster, high adhesive force	inner/outer coating

Usage:

1. According to the construction process, can be specified by adding diluent conditioning solid content and Viscosity. to control the thickness of the coating, usually adjusted for spraying viscosity 15-25 seconds; diluent should not contain water, sulfur and other impurities. The coating adhesive force will be affected, so was stem and other properties.
2. When in use, it should be avoided with acid and alkali, organic acids and amines contact, otherwise it will accelerate ageing, affect the performance of the product.
3. At work, according to the resin NO and the use of different requirements and then confirm dying condition, for high temperature dying type, it should be solvent dying to volatile at a lower temperature (120 or 160 ° C). Finally curing at 220 ºC.
4. Resin has good compatibility with heat resistant pigments (aluminum, glass bead, low-density ceramic powder. Black chromium oxide and iron oxide powder, etc.), the coating should be dipping, spraying, brush and other construction methods, curing the coating can be used in 250-400 ºC. Some may be resistant 500-600 ° C, even higher temperatures.
5. Application examples of reference:
(1) fire-resistant insulation coating formula : 

silicone resin	Higher chlorinated polyethylene	epoxy resinF-644	Polyamide resin	Padding	Flux	Titanate
40-60Copies	5-15Copies	10-20Copies	4-12Copies	45-85Copies	5-15Copies	1-2Copies

 

All material will be transferred into a paste, and then grinding with sand mill 20 ~ 30min after the addition of solvent dispersion, and then filter.
(2) fire-resistant aluminum section formula :

60% Methylphenyl silicone resin	65%Aluminum Paste	xylene	Dispersant
76Copies	26Copies	46Copies	2Copies

Put aluminum paste into a container, add a small amount of resin, stir slowly, add disperser and residual resin, added xylene to construction of viscosity after fully stirred, with 120 mesh silk filter then finish.

Safety Note :
1. Resin contains flammable, explosive and toxic solvents, In the process of use and processing, should pay attention to the site operation ventilation, to prevent fire, strengthening the protection of workers.
2. During transportation and storage, prevent sunlight, fire and heat protection, pay attention to warehouse ventilation.
3. Packed with galvanized iron sheet barrel, storage period is generally 6 months, if pass storage period, please test it strictly and then use. Avoid heat, otherwise it will reduce the storage stability.