Iota M3050j Self-Adhesive High Transparent Liquid Silicone Rubber Used in Sealing of Swimming Goggles/Mobile Phone Protective Case Rubber Coating

• Appearance: Liquid
• Usage: Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
• Color: White
• Density 23ºC: 1.13 g/cm3
• Hardness (Shore a): 50
• Tensile Strength: 10.0MPa
• Model NO.: Self-adhesive high transparent liquid silicone rub
• Elongation: 550%
• Transport Package: Component a: 200 Kg/Drum, Component B: 200 Kg/Drum
• Specification: Component A: 200 Kg/drum, component B: 200 Kg/drum
• Trademark: iota
• Origin: Bengbu Anhui China
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

Self-adhesive high transparent liquid silicone rubber IOTA M3050J

Description

IOTA M3050J A/B is a high transparent liquid silicone rubber with self-adhesive property to PC, and has good mold release performance.

 

Features

Two component, 1:1 mixing ratio

Excellent mold release

Excellent transparency

Excellent self-adhesion to PC

Rapid thermal curing

Excellent mechanical properties 

 

Applications

Sealing of swimming goggles

Mobile phone protective case rubber coating

Smart watch back cover sealing ring

Mobile phone card holder seal, etc

 

NOTES 

1. IOTA M3051J is a platinum catalyzed product. The platinum catalyst is in the component A. Strict attention should be paid when using, to avoid catalyst poisoning. 

2. Only components A and B of the same lot number can be mixed together.

3. To ensure optimum fluidity and homogeneity of the material, the material must be thoroughly agitated before being transferred to the container to disperse any sedimentation that may occur during the storage period. 

 

Technical index:   

Properties	Test Method	Value
uncured
Component A
Viscosity at 23ºC, stirred	ISO3219	300mPa.s
Component B
Viscosity at 23ºC, stirred	ISO3219	400mPa.s
Product data (A+B mixed)
Viscosity at 23ºC, stirred	ISO3219	350mPa.s
Curing time		See curing conditions
Product data (after cured)	(23±2ºC, after curing for 24h)
Density 23ºC		1.13 g/cm^3
Hardness (Shore A)	DIN 53505	50
Tensile Strength	DIN 53504	10.0MPa
Elongation	DIN 53504	550%
Tear Strength		35KN/m

 

Packaging

Component A: 200 Kg/drum, component B: 200 Kg/drum.

 

Storage  

1. Below 23°C, unopened barrels can be stored for 12 months, and the best use-by date is marked on the label of each product's outer packaging.

2. After the expiry date, it is necessary to do performance tests for relevant indicators to ensure the quality, and then could be used.