Iota-5118ab Silicone Gel Chemicals for Potting a Variety of Automotive and Electronic Components

• Type: Synthesis Material Intermediates
• Appearance: Hyaline Gel
• Quality: Refined
• Model NO.: IOTA-5118AB
• Colour: Colorless
• Glue Viscosity (Precure): a:1600MPa.S B:1300MPa.S
• Glue Mixing Viscosity(Precure): 1400MPa.S
• Glue Density(Precure): 0.97g/cm3
• Refractive Index(Precure): 1.404
• Transport Package: Drum
• Specification: 15/180kg
• Trademark: IOTA
• Origin: China
• HS Code: 3910000000
• Production Capacity: 500t/Month

Product Description

Silicone gel IOTA-5118AB

intro

IOTA-5118AB is a low viscosity additive formed two-component room temperature curing silicon gel, which has good fluidity before curing. After curing with a mixture ratio of 1:1, silicon gel with very low hardness can be quickly heat-cured. The silicone gel has a completely transparent appearance, good surface viscosity, and excellent mechanical damping properties. In addition, IOTA-5118AB can change the mixing ratio of AB agent according to different application conditions to obtain silicon gels with different hardness to meet different application requirements.

Application field
Bond the display's glass cover and polarizer
Potting a variety of automotive and electronic components
Solar cell potting
Damped product

Product performance parameter

IOTA 5118AB
	Item	Test instruments and methods	Test result
Precure	Appearance color	Visual inspection	A: Colorless and transparent B: Colorless and transparent.
	Glue viscosity	ISO 3219	A:1600mPa.s B:1300mPa.s
	Glue mixing viscosity	ISO 3219	1400mPa.s
	Glue density	GB/T4472-2011	0.97g/cm3
	Refractive index	GB/T 6691-1986(25ºC)	1.404
	Operational time	25ºC	1.5h
solidify	Mixing ratio	A:B	1:01
	Curing condition	oven	150ºC/30min
After curing	Appearance	Visual inspection	Hyaline gel
	Light transmittance	GB/T 2410-2008	>99%
	Needle penetration	DIN ISO 2137	250 1/10min
	Relative dielectric constant (50Hz)	IEC 60250 100KHz	2.7
	Volume resistance	IEC 93	1016 o
	Surface resistance	IEC 93	1014 o
	Dielectric loss (50Hz)	VDE0303 T4/50Hz	10X10-4
	Refractive index	nD 25	1.404
	Dielectric strength	IEC 243	23 kV/mm

Surface treatment
All substrates to be constructed shall undergo a surface cleaning process to ensure that the silicon gel can cure normally. The main substances that cause abnormal solidification of silicon gels are sulfur containing substances, plasticizers, polyurethanes, ammoni- containing substances, phosphorus containing substances and organometallic compounds (such as tin and lead). When it is not known whether the substrate surface is a toxic catalyst, a small amount of substrate should be selected for curing test.

Mixed
IOTA-5118AB contains A catalyst in component B and A crosslinker in component A. The two components can be mixed 1:1 by volume ratio or mass ratio. Bubbles will be generated in the process of mixing or dispensing, so it needs to be debubbled by a vacuum debubbling process.

Solidify
IOTA-5118A/B can select different curing temperatures according to different application conditions. The higher the temperature, the faster the curing speed. Different curing temperatures such as 25ºC, 100ºC and 150ºC can be selected.

Storage condition
IOTA-5118A/B keeps the factory sealed original packaging and can be stored at least 6 months at 5-30ºC. If the product exceeds its shelf life, it can be used with caution after critical quality testing.

Matters needing attention
1. IOTA-5118A/B must not contain direct contact with phosphorus (P), sulfur (S), nitrogen (N), organotin (Sn), water, polyurethane, acrylate compounds and other catalytic poisons during use and storage, so as to avoid the phenomenon of curing obstruction and deterioration.
2. Only when the A and B components are the same batch number can they be mixed.
3. When dispensing glue manually, pay attention to the cleaning of the mixing tools, and pay special attention to avoid contaminating agent A or agent B in the rubber bucket through the dispensing tools.
4. The mixed glue should be used up within the prescribed time as far as possible, and the glue mixed by hand should be used up within 1h; The glue in the automatic mixing machine should pay attention to the regular discharge of glue, otherwise it is easy to cause the glue to not cure.
5. IOTA-5118A/B is sensitive to heat, and high temperature should be avoided during storage and operation. After the use of agent A and agent B, the unused glue can not be poured into the original package, so as not to pollute the unused glue.
6. After IOTA-5118A/B two-component mixture, the gel will slowly cure at room temperature. Before use, the product should be weighed after determining the amount of use to avoid waste.
7. If the gel is too soft or sticky, a harder gel can be obtained by reducing the amount of component B. The ratio of A:B can be 1.1:1, 1.2:1, 1.3:1, 1.4:1, 1.5:1, 1.6:1, etc.
8. If the product needs to be dyed, the required dye can be added to the product and mixed evenly to obtain silicon gel of different colors.


Package
A:15KG/ barrel; B:15KG/ barrel
A:180KG/ barrel; B:180KG/ barrel