Iota M1740 Special Coating Liquid Silicone Rubber for Airbag for Airbag Coating/Architectural Textile Coating/Protective Clothing Coating/3c Product Sealing

• Appearance: Liquid
• Usage: Oil Drilling Auxiliary Agent, Water Treatment Chemicals, Rubber Auxiliary Agents, Plastic Auxiliary Agents, Coating Auxiliary Agents, Textile Auxiliary Agents, Paper Chemicals, Surfactants, Leather Auxiliary Agents, Electronics Chemicals
• Color: Yellow
• Density at 23ºC: 1.07 g/cm3
• Hardness: 35
• Tensile Strength: 5.0 MPa
• Model NO.: Special coating liquid silicone rubber for airbag
• Elongation at Break: 350%
• Tear Strength: 10 Kn/M
• Transport Package: Component a: 10 Kg/Drum, Component B: 200 Kg/Drum
• Specification: Component A: 10 Kg/drum, Component B: 200 Kg/drum
• Trademark: iota
• Origin: Bengbu Anhui China
• HS Code: 391000
• Production Capacity: 800t/Moth

Product Description

Special coating liquid silicone rubber for airbag IOTA M1740

Description

IOTA M1740 A/B is a special coating liquid Silicone rubber for airbag with self-adhesive properties to PA66. 

 

Advantages

Excellent self adhesion to PA66

low viscosity and easy automatic feeding

Rapid heat curing

long operation time after mixing

Excellent mechanical properties

 

Application

Airbag coating

Architectural textile coating

Protective clothing coating

3C product sealing, etc

 

Curing condition

Temperature: 160°C

Curing time:T90 less than 25s

 

Note

IOTA M1740 A/B is a platinum catalyzed product. The platinum catalyst is in the component A. Strict attention should be paid when using, to avoid catalyst poisoning.

 

Packing and storage

Component A:200kg/iron drum, component B:200kg/iron drum

 

Storage

1. Below 23°C, unopened barrels can be stored for 12 months, and the best use-by date is marked on the label of each product's outer packaging.

2. After the expiry date, it is necessary to do performance tests for relevant indicators to ensure the quality, and then could be used.

 

Technical index

Properties	Test method	Value
Unmixed
Component A
Color		slight yellow
Density		1.07 g/cm^3
Viscosity at 25ºC,0.9S^-1	Brookfield	45000 mPa.s
Component B
Color		Milk white
Density		1.07 g/cm^3
Viscosity at 25ºC,0.9S^-1	Brookfield	53000 mPa.s
Technical data(A+B mixed)
Mix ratio(weight)	A:B	1:1
Viscosity at 25ºC,0.9S^-1	Brookfield	52000 mPa.s
Curing time		See curing conditions
Technical data(cured)	165±2ºC*300 S
Color		slight yellow
Density at 23ºC	DIN EN ISO 1183	1.07 g/cm^3
Hardness	DIN ISO 48-4	35
Tensile strength	ISO 37 type 1	5.0 Mpa
Elongation at break	ISO 37 type 1	350%
Tear strength	ASTM D 624 B	10 KN/m