Audited Supplier Polyester modified silicone resin IOTA-1038A
Resin properties and uses:
This product has excellent high temperature performance and water repellent and moisture resistant performance and good electrical insulation properties, arc corona resistance performance. Its weather resistance and chemical stability is also very good. This product has high hardness, high gloss, good fullness, high anti-yellowing performance after fully cured (more than 3H).
IOTA-1038A widely use as high temperature resistant coating, recommended for electric rice cooker, oven, baking bread machine, electric iron, range hood, gas stove and other household electrical appliances, such as temperature resistant non-stick coating and special coating of basic resin.
Curing method:
This product uses the high temperature curing, 250ºC for 20 min; 270ºC for 15 min; 280ºC for 10 min.
Index:
|
Appearance:
|
Colorless to light yellow transparent liquid, no mechanical impurities
|
|
Viscosity, cst (closed 4 cup):
|
270-500
|
|
Solid content,%:
|
59±1
|
|
Curing conditions:
|
Fully cured with 250°C for 20mins, 280°C for 10mins.
|
|
Acid value:
|
4-8mgKOH/g
|
|
Solvent:
|
PMA
|
Attentions:
a.The diluted solvent used for this product shall not contain water, pyridine and impurities containing sulfur compounds, otherwise it will affect the adhesion, dry and other properties of the resin paint film..
b.This product in the processing process, there will be a large number of xylene and other flammable and explosive, toxic solvents volatile out, should pay attention to strengthen the field of ventilation, pay attention to fire, strictly avoid the fire source. Operator should pay attention to labor protection.
c.This product is used in the process of processing equipment, containers must be clean. To prevent dust and foreign bodies and mixed with water.
d.Acid, alkali, salt of organic acid and amine compounds have accelerated curing effect on this product, and affects heat resistance and electric properties. Therefore, this product should be kept in strict isolation from these substances.
Storage:
The product storage period is tentatively scheduled for half a year. This product should be stored in a cool,dry and ventilated place, prevent sun direct radiation; prevent the serious pollution of acid, alkali and should be cut off from the source of the fire and away from the heat source.