IOTA M8760 A/B is a flowable, addition-type, two components, room temperature curing thermally conductive silicone rubber.
Features
Two-component, 1:1 mix ratio
Low viscosity, easy foaming, good leveling
Good thermal conductivity
Good heat resistance, moisture resistance, cold resistance
Flame retardant up to UL94-V0 level
Strong adhesion
No by-products are produced during curing reaction
Applications
Potting of automotive and power and electronic components
Solar Potting
Mechanical Bonding and Sealing of Electronic Components
Thermally conductive products
Curing
|
Temperature |
Curing time, 1cm thickness |
|
23ºC |
8h |
|
100ºC |
15 min |
|
150ºC |
5 min |
NOTES
1. IOTA M8760 is a platinum catalyzed product. The platinum catalyst is in the component A. Strict attention should be paid when using, to avoid catalyst poisoning.
2. Only components A and B of the same lot number can be mixed together.
3. To ensure optimum fluidity and homogeneity of the material, the material must be thoroughly agitated before being transferred to the container to disperse any sedimentation that may occur during the storage period.
Technical index:
|
Properties |
Test Method |
Value |
|
uncured |
|
|
|
Component A |
|
|
|
color |
|
grey |
|
Density 23ºC |
|
1.6 g/cm3 |
|
Viscosity at 23ºC, stirred |
ISO3219 |
5000mPa.s |
|
Component B |
|
|
|
color |
|
white |
|
Density 23ºC |
|
1.6 g/cm3 |
|
Viscosity at 23ºC, stirred |
ISO3219 |
4000mPa.s |
|
Product data (A+B mixed) |
|
|
|
Mixing ratio (weight) |
A:B |
1:1 |
|
Viscosity at 23ºC, stirred |
ISO3219 |
4500mPa.s |
|
Room temperature operation time |
23±2ºC |
2h |
|
Curing time |
|
See curing conditions |
|
Product data (after cured) |
(23±2ºC, after curing for 24h) |
|
|
color |
|
grey |
|
Density 23ºC |
|
1.6 g/cm3 |
|
Hardness (Shore A) |
DIN 53505 |
60 |
|
Tensile Strength |
DIN 53504 |
2.0MPa |
|
Elongation |
DIN 53504 |
150% |
|
Thermal Conductivity |
GB/T 10297-1998 |
0.7 W/m.K |
|
Dielectric Strength |
IEC243 |
23 KV/mm2.8 |
|
Volume Resistance |
IEC93 |
1015 Ω cm |
Packaging
Component A: 25 Kg/drum, component B: 25 Kg/drum.
Storage
1. Below 23°C, unopened barrels can be stored for 12 months, and the best use-by date is marked on the label of each product's outer packaging.
2. After the expiry date, it is necessary to do performance tests for relevant indicators to ensure the quality, and then could be used.