Raw Material: | Synthetic Rubber |
---|---|
Material: | Silicone Rubber |
Appearance: | Solidity |
Form: | Solidity |
Type: | Vmq |
Density at 25 C, g/cm3, Approx: | 1.22 |
Samples: |
---|
Suppliers with verified business licenses
HEAT CURED SILICONE RUBBER IOTA HCR 1970 U
Description: IOTA HCR 1970 U is a silicone master-batch, heat curing after the addition of a vulcanizing agent (chosen according to the processing method).
Applications: IOTA HCR 1970 U is recommended for moulding, has good compromise of mechanical properties.
Special properties:
Good mechanical properties;
Good appearance, anti-yellowing;
Good heat stability, up to 200°C;
Not easy to structured after long-term storage;
No post curing or slight post curing;
Wide possibilities for blending with other master batch.
Characteristics
Type (in accordance with GB/T 5576-1997) .................. VMQ
Density at 25°C, g/cm3, approx...........................… 1.22
Natural color....................................… translucent
Properties after working:
1) After addition of 1.25% Di(2,4-dichlorobenzoyl) peroxide (at 50%), and vulcanization for 8 minutes at 115ºC
2) After addition of 1.1% 2,5-dimethyl-2,5-di(tert-butylperoxy)hexan- (at 45%), and vulcanization for 5 minutes at 175ºC
1.Mechanical property:
1.1 Properties without post-cure 1) 2)
Shore A hardness, approx..............................… 69 69
Tensile strength, MPa, approx...........................… 7.3 8.4
Elongation at break, %, approx............................ 372 399
Modulus at 100% elongation, MPa, approx...............…. 2.64 2.68
Tear strength, (ASTM D 624 Die B) kN/m, approx.........… 19 19
Rebound resilience, %, approx........................… 43 42
Linear shrinkage, %, approx...........................… 1.5 3.2
1.2Properties after post-cure for 4 hours at 200°C
Shore A hardness, approx...........................… 71 73
Tensile strength, MPa, approx.......................... 8.2 8.8
Elongation at break, %, approx........................ 326 358
Modulus at 100% elongation, MPa, approx............... 3.00 2.93
Tear strength (ASTM D 624 Die B),kN/m, approx......… 16 17
Compression set , (22 h/177ºC/25%) %, approx......... - 27
Rebound resilience, %, approx........................ 40 42
Linear shrinkage, %, approx........................... 2.1 3.8
2. Thermal stability
Properties after post-cure for 3 days at 225°C
Shore A hardness, approx...........................… 74 76
Tensile strength, MPa, approx.......................... 6.4 6.1
Elongation at break, %, approx........................… 11 204
Packaging: IOTA HCR 1970 U is delivered in 20 kg carton boxes.
Storage and shelf life: IOTA HCR 1970 U may be stored in its original unopened packaging at a temperature below 40°C for up to 12 months from the date of manufacture marked clearly on the packaging.
Past this date, IOTA no longer guarantees that the product meets the sales specifications.
Suppliers with verified business licenses